How to Safely Use High Temperature Resistant Glass
1. Reasons for cracking of high temperature resistant glass: The surface of steel (reinforced) glass is a compressive stress layer, while the internal tension stress layer corresponds to it and keeps balance. When the surface scar extends to the internal tension stress layer, it will cause fracture. This scar can be divided into several types:
(1) Scars caused by collision of hard objects, sparks during fusion, flying objects, etc.
(2) Glass collision during handling and storage.
(3) Glass damage during mounting.
(4) Failure of thermal stress and system stress.
(5) External impact.
(6) Scars caused by accidental ionization in glass.
2. As long as the high-temperature glass is partially damaged and cracked, it will lose the balance of stress, and cause overall cracking. Some of the fragments are scattered into granules, while others are still attached to each other and become aggregated fragments. When a rupture occurs, a person nearby may be impacted by a large aggregate of debris, such as a large aggregate of debris, which may injure the human body.
3. Cutting or drilling of high temperature resistant glass: After cutting or drilling, the strengthening of the surrounding tissues of glass will be greatly weakened, and such processing should be avoided as far as possible in the parts bearing large external forces; if it is not necessary to process, the reinforced glued glass should be selected.
4. When using high temperature glass in the following parts, it is desirable to use steel (reinforced) glued glass:
(1) The glass used in the roof, skylight and daylighting skylight of the patio in horizontal or near horizontal state.
(3) The exterior wall of the building is used vertically. If it falls, it will damage the glass of objects and human bodies on the ground.
Handrails or guards, such as glass, which may cause the body or object to fall when broken.
OBJECTIVE: To increase the strength of glass and its ability to withstand pressure and temperature difference. Ensure consumer safety.
Uses: Widely used in various areas of life.
Notes: 1. Strictly control the production of steel pitting points and silver bars. 2. Within the scope of national standard for steel bending control, the bending degree of matching products should be reduced as far as possible.
If you are interested in the borosilicate glass or need to consult, please click on our online customer service, or call us.
Pan Chao, customized different quality specifications of the glass.
Pan Chao special industrial glass, tailored for your different quality of the glass.
Welcome sending your inquiry: Phone : +86 13343800331 Email: info@panchaoglass.com
Related articles
- What is the difference between float tempered glass and ordin
- What should be paid attention to when using quartz glass
- What are the advantages of high borosilicate glass water cups
- How to clean optical glass lenses disc daily?
- What are the advantages of smart switch glass panels
- Quartz glass tube high temperature tube furnace high purity t
- high borosilicate custom logo glass extracter tube glass test
- Brief introduction of glass production process
- customized ultra-white 1.0mm 2mm 3mm square glass sheet,squar
- What are the benefits of processing glass with quartz square
Products
acrylic display center
Contact Us
Xinxiang Pan Chao Instruments Co., Ltd.
Tel: +86 13343800331
Contact person:Carrie Niu
Fax: 0373 303 0331
Email:sales@panchaoglass.com